Interaction of NO2 with TiO2 surface under UV irradiation: measurements of the uptake coefficient

ADD TO MY LIST
 
Author(s): A. El Zein | Y. Bedjanian

Journal: Atmospheric Chemistry and Physics
ISSN 1680-7316

Volume: 12;
Issue: 2;
Start page: 1013;
Date: 2012;
VIEW PDF   PDF DOWNLOAD PDF   Download PDF Original page

ABSTRACT
The interaction of NO2 with TiO2 solid films was studied under UV irradiation using a low pressure flow reactor (1–10 Torr) combined with a modulated molecular beam mass spectrometer for monitoring of the gaseous species involved. The NO2 to TiO2 reactive uptake coefficient was measured from the kinetics of NO2 loss on TiO2 coated Pyrex rods as a function of NO2 concentration, irradiance intensity (JNO2 = 0.002–0.012 s−1), relative humidity (RH = 0.06–69 %), temperature (T = 275–320 K) and partial pressure of oxygen (0.001–3 Torr). TiO2 surface deactivation upon exposure to NO2 was observed. The initial uptake coefficient of NO2 on illuminated TiO2 surface (with 90 ppb of NO2 and JNO2≅0.006 s−1) was found to be γ0 = (1.2±0.4) ×10−4 (calculated using BET surface area) under dry conditions at T = 300 K. The steady state uptake, γ, was several tens of times lower than the initial one, independent of relative humidity, and was found to decrease in the presence of molecular oxygen. In addition, it was shown that γ is not linearly dependent on the photon flux and seems to level off under atmospheric conditions. Finally, the following expression for γ was derived, γ = 2.3×10−3 exp(−1910/T)/(1 + P0.36) (where P is O2 pressure in Torr), and recommended for atmospheric applications (for any RH, near 90 ppb of NO2 and JNO2 = 0.006 s−1).
Save time & money - Smart Internet Solutions      Why do you need a reservation system?