Preparation and Characterization of Silica-Coated Magnetic–Fluorescent Bifunctional Microspheres

ADD TO MY LIST
 
Author(s): Xiao Qi | Xiao Chong

Journal: Nanoscale Research Letters
ISSN 1931-7573

Volume: 4;
Issue: 9;
Start page: 1078;
Date: 2009;
Original page

Keywords: Bifunctional microspheres | Magnetic | Fluorescent

ABSTRACT
Abstract Bifunctional magnetic–fluorescent composite nanoparticles (MPQDs) with Fe3O4MPs and Mn:ZnS/ZnS core–shell quantum dots (QDs) encapsulated in silica spheres were synthesized through reverse microemulsion method and characterized by X-ray powder diffraction, scanning electron microscopy, transmission electron microscopy, vibration sample magnetometer, and photoluminescence (PL) spectra. Our strategy could offer the following features: (1) the formation of Mn:ZnS/ZnS core/shell QDs resulted in enhancement of the PL intensity with respect to that of bare Mn:ZnS nanocrystals due to the effective elimination of the surface defects; (2) the magnetic nanoparticles were coated with silica, in order to reduce any detrimental effects on the QD PL by the magnetic cores; and (3) both Fe3O4MPs and Mn:ZnS/ZnS core–shell QDs were encapsulated in silica spheres, and the obtained MPQDs became water soluble. The experimental conditions for the silica coating on the surface of Fe3O4nanoparticles, such as the ratio of water to surfactant (R), the amount of ammonia, and the amount of tetraethoxysilane, on the photoluminescence properties of MPQDs were studied. It was found that the silica coating on the surface of Fe3O4could effectively suppress the interaction between the Fe3O4and the QDs under the most optimal parameters, and the emission intensity of MPQDs showed a maximum. The bifunctional MPQDs prepared under the most optimal parameters have a typical diameter of 35 nm and a saturation magnetization of 4.35 emu/g at room temperature and exhibit strong photoluminescence intensity.

Tango Rapperswil
Tango Rapperswil

     Save time & money - Smart Internet Solutions