SiC Nanorods Grown on Electrospun Nanofibers Using Tb as Catalyst: Fabrication, Characterization, and Photoluminescence Properties

ADD TO MY LIST
 
Author(s): Zhou Jin-Yuan | Chen Zhi-Yong | Zhou Ming | Gao Xiu-Ping | Xie Er-Qing

Journal: Nanoscale Research Letters
ISSN 1931-7573

Volume: 4;
Issue: 8;
Start page: 814;
Date: 2009;
Original page

Keywords: SiC nanorods | Vapor-liquid-solid mechanism | Terbium | Electrospinning | Photoluminescence

ABSTRACT
Abstract Well-crystallizedβ-SiC nanorods grown on electrospun nanofibers were synthesized by carbothermal reduction of Tb doped SiO2(SiO2:Tb) nanofibers at 1,250 °C. The as-synthesized SiC nanorods were 100–300 nm in diameter and 2–3 μm in length. Scanning electron microscopy (SEM) results suggested that the growth of the SiC nanorods should be governed by vapor-liquid-solid (VLS) mechanism with Tb metal as catalyst. Tb(NO3)3particles on the surface of the electrospun nanofibers were decomposed at 500 °C and later reduced to the formation of Tb nanoclusters at 1,200 °C, and finally the formation of a Si–C–Tb ally droplet will stimulate the VLS growth at 1,250 °C. Microstructure of the nanorod was further investigated by transmission electron microscopy (TEM). It was found that SiC is the preferred initial growth direction. The liquid droplet was identified to be Si86Tb14, which acted as effective catalyst. Strong green emissions were observed from the SiC nanorod samples. Four characteristic photoluminescence (PL) peaks of Tb ions were also identified.