Author(s): Yarram Chetty Venudhar | Katrapally Vijaya Kumar | Gopathi Ravi Kumar
Journal: Advances in Molecular Imaging
ISSN 2161-6728
Volume: 03;
Issue: 02;
Start page: 87;
Date: 2012;
Original page
Keywords: Ferrite | High Sintering Temperature | X-Ray Diffractograms | Spinel Structure | SEM | Magnetic Properties
ABSTRACT
The Ni1–xCuxFe2O4 (x = 0.0, 0.1, 0.2, 0.3, 0.4, 0.5, 0.6, 0.7, 0.8, 0.9, 1.0) ferrites have been prepared by sol-gel method in order to obtain homogeneous crystal structure and they are sintered at high temperature. The effect of copper doping on the structural and magnetic properties of nickel ferrites sintered at 1000°C has been examined. The X-ray diffraction measurements clearly showed the formation of single phase spinel ferrite structure in all the prepared ferrite compositions. Because of the high sintering temperature the particle size is observed beyond the nano-scale range in all the compositions. The lattice parameters are found to increase with increasing doping concentration of the copper content. Magnetization results exhibit a non-collinear ferrimagnetic structure for x = 0.0 to 0.5 and Neel’s collinear ferrimagnetic structure for x = 0.5 to 0.9 suggesting a change in magnetic ordering.
Journal: Advances in Molecular Imaging
ISSN 2161-6728
Volume: 03;
Issue: 02;
Start page: 87;
Date: 2012;
Original page
Keywords: Ferrite | High Sintering Temperature | X-Ray Diffractograms | Spinel Structure | SEM | Magnetic Properties
ABSTRACT
The Ni1–xCuxFe2O4 (x = 0.0, 0.1, 0.2, 0.3, 0.4, 0.5, 0.6, 0.7, 0.8, 0.9, 1.0) ferrites have been prepared by sol-gel method in order to obtain homogeneous crystal structure and they are sintered at high temperature. The effect of copper doping on the structural and magnetic properties of nickel ferrites sintered at 1000°C has been examined. The X-ray diffraction measurements clearly showed the formation of single phase spinel ferrite structure in all the prepared ferrite compositions. Because of the high sintering temperature the particle size is observed beyond the nano-scale range in all the compositions. The lattice parameters are found to increase with increasing doping concentration of the copper content. Magnetization results exhibit a non-collinear ferrimagnetic structure for x = 0.0 to 0.5 and Neel’s collinear ferrimagnetic structure for x = 0.5 to 0.9 suggesting a change in magnetic ordering.